Oleamide

1, mainly used for the CPP, BOPP, LDPE, LLDPE, EVA, PVC, PVDF, PVDC, PU and metallocene polyethylene plastic, such as agents and anti-tackifier can significantly reduce the product (film or sheet) surface dynamic and static coefficient of friction to improve the ease of processing and packaging efficiency. 
2, in the ink from, anti-adhesive role of anti-fouling, delayed pigment, filler caking settlement and to help re-distributed to increase the prints resistance to abrasion, scratch resistance, as well as the smooth surface, especially to improve the its and anti-color printing viscosity. 
3, in the rubber (SBE, SBP, SBR, PP) added to the goods, rubber products can increase the gloss, anti-fouling and elongation, and enhanced wear resistance to promote curing, in particular to prevent the effects of the sun cracks . 
4, used as a thermoplastic elastomer (TPE, TEO, TPU) and fluoride release agent and the surface of rubber and brightener, lubricant and release agent engineering plastics, LDPE leather rolling lubricant, fiber material, non - Textile fabrics and entertainment agent chips. 
5, for the ink to provide good anti-wear, anti-scratch, anti-slip and increasing degree of surface performance, to avoid the printing process at a high speed friction and wear and tear film with each other and the impact of the printed ink surface effect, the elimination of high-speed printing process ink film easily detached the phenomenon in the roller to increase ink and surface finish, but also to improve the crystal surface of ink in the printing subsidiary, anti-adhesive, anti-scratch and anti-permeability of India, making Western clear, bright color.

Content (%)                           99.8%
Iodine value (gI2/100g)       ≤ 80-95 
Acid value (mgkoh/g)             ≤ 0.3 
Melting Point (°C)                  70-78 
Chroma (Hazen)                    ≤ 100 
Moisture (wt%)                       ≤ 0.3 
Impurities Φ0.1-0.2 (mm)         ≤ 1       

20,25 Kg / bag or 1000Kg / tray. 

14tons per 20’GP